TORAY PLA resin Ecodear

Type Feature
General Purpose V751X52
  • Heat resistance, High impact
  • Bio-based content 30%
Flame Retardant V554R10
  • Non-halogen, UL94 V-0
  • Bio-based content 25-30%
V554X51
  • Non-halogen, UL94 5VB
  • Bio-based content 25-30%
Specialty V911X51
  • Transparency, Heat resistance
  • Bio-based content 30%

General Purpose- Heat resistance, high impact

Properties Test
Method
Unit TORAY PLA resin
"Ecodear"
ABS
(TOYOLAC 700)
V751X52(CA05-051)
Tensile Strength ISO 527 MPa 52 54
Elongation at break % 10 18
Flexural Strength ISO 178 MPa 73 81
Flexural Modulus GPa 2.3 2.5
Charpy Impact Strength ISO 179 kJ/m2 20 17
DTUL (0.45 MPa) ISO 75 0C 79 95
MFR (220 degreeC, 10kg) ISO 1133 g/10 min 13 23
Density ISO 1183 Kg/m3 1140 1050
Mold shrinkage - % 0.4-0.6 0.4-0.6

Halogen Free Flame Retardant grade

Properties Test
Method
Unit V554R10 V554X51 PC//ABC
(Flame retardant
type)
Flammability(1.5mm) UL-94 - V-1 V-0 V-0
Flammability(2.0mm) UL-94 - V-1 5VB V-0
Flammability(3.0mm) UL-94 - V-0 5VB V-0
Tensile Strength ISO 527 MPa 67 67 61
Elongation at break % 20 20 40
Flexural Strength ISO 178 MPa 98 97 95
Flexural Modulus GPa 3.6 3.5 2.8
Charpy impact (notched) ISO 179 kJ/m2 8 7 27
DTUL(0.45MPa) ISO 75 degree C 84 78 94
MFR(240 degreeC,2.16kg) ISO 1133 g/10min 7 10 -
Density ISO 1183 Kg/m3 1270 1270 1210
Mold shrinkage - % 0.4-0.6 0.4-0.6 0.4-0.6



.