TORAY PPS A512-X02N3

GF10%, Low Wear and Friction, Flame retardant

Property Test Condition Test Methhod ISO Units Short carbon fiber reinforced P
PS
GF10%, Low Wear and Friction
Flame retardant
A512-X02N3
>PPS-CF10<
Physial property
Glass Fiber contents     wt% 10
Water Absorption 230Cx50%RH in water   % -
Density 230C ISO1183 kg/m3 1515
Mechanical property
Tensile strength 230C ISO527-1,2 MPa 110
Elongation at Break 230C ISO527-1,2 % 1.5
Flexural Strength 230C ISO178 MPa 156
Flexural Modulus 230C ISO178 GPa 9.4
Coefficient of friction Vs S45C, 1MPa, 0,33m/s Suzuki Method - 0.15
Coefficient of friction Vs SUS, 1MPa, 0,33m/s Suzuki Method - 0.06
Amount of wear Vs S45C, 1MPa, 0,33m/s Suzuki Method mg/h 0.2
Amount of wear Vs SUS, 1MPa, 0,33m/s Suzuki Method mg/h 0.5
Limit of PV Vs S45C Suzuki Method MPa.m/s 2.9
Limit of PV Vs SUS Suzuki Method MPa.m/s 2
Charpy Impact Strength (V-notched) 230C ISO179 kj/m2 4.7
Heat property
Melting Point   DSC Method 0C 278
Coef of Linear Thermal Expansion   ISO11359-2 x10-5/C 2.1
Heat Deffection Temp High Load 1.80MPa ISO75-1,2 0C 260
Flammability   UL94 rank/thickness m mt V-0Equivarent
Electrical property
Volume Resistivity   IEC60093 &Omega.m 101
Molding property
Mold shrinkage MD 80x80x3mmt Toray method % 0.2
Mold shrinkage TD 80x80x3mmt Toray method % 0.8

a) MD; Machine direction, TD; Transverse direction

.